CMP process leaving no residual oxide layer or slurry particles

ABSTRACT

Two problems seen in CMP as currently executed are a tendency for slurry particles to remain on the surface and the formation of a final layer of oxide. These problems have been solved by adding to the slurry a quantity of TMAH or TBAH. This has the effect of rendering the surface being polished hydrophobic. In that state a residual layer of oxide will not be left on the surface at the conclusion of CMP. Nor will many slurry abrasive particles remain cling to the freshly polished surface. Those that do are readily removed by a simple rinse or buffing. As an alternative, the CMP process may be performed in three stages—first convention CMP, then polishing in a solution of TMAH or TBAH, and finally a gentle rinse or buffing.

FIELD OF THE INVENTION

[0001] The invention relates to the general field of chem-mech polishing with particular reference to controlling the state of the final surface.

BACKGROUND OF THE INVENTION

[0002] Chemical mechanical polishing (CMP) is now widely used in the semiconductor manufacturing industry as the method of choice for planarizing any given layer prior to the deposition of the next layer. As an example, consider a dielectric layer 11, as shown schematically in FIG. 1, in which a cavity 13 has been formed and then over-filled with a layer of a metal 12, such as tungsten or copper.

[0003] To perform CMP a slurry of abrasive particles (typically SiO₂ or Al₂O₃ particles) having a mean diameter between about 1 and 10,000 microns) suspended in an aqueous solution of hydrogen peroxide and nitric acid, is used. The hydrogen peroxide oxidizes the surface that is being polished thereby forming a brittle layer of oxide that is readily dislodged by the suspended particles.

[0004] Although the CMP process as described above works well in many respects, a few problems still remain. Two such problems are illustrated in FIG. 2. The first is exemplified by slurry particles 24, some of which tend to remain on the surface of the metal at the conclusion of CMP. These have to be removed in a separate operation and can often remain in place when not expected to. The second problem is exemplified in layer 23 which represents a final layer of oxide that remains at the conclusion of CMP. When processing continues, layer 23 may remain in place and increase the contact resistance to the next metal layer, as shown in FIG. 3 where oxide layer 23 has become interposed between the two metal plugs 12 and 31, the latter being contained within a second dielectric layer 32.

[0005] There is therefore a need for a CMP process wherein no oxide layer remains on the surface of a metal after CMP and wherein no particles of abrasive material remain either. Preferably such a process would be part of the standard CMP process as currently used so as to introduce minimum disruption into the overall manufacturing process.

[0006] A routine search of the prior art was performed with the following references of interest being found:

[0007] In U.S. Pat. No. 5,662,769, Schonauer et al. show a tungsten CMP process and post clean. In U.S. Pat. No. 6,165,956, Zhang et al. show a tungsten CMP together with NH₄OH brushing in the background section. U.S. Pat. No. 5,968,280 (Ronay) shows a poly-electrolyte post CMP clean. While U.S. Pat. No. 5,868,863 (Hymer et al.) and U.S. Pat. No. 6,207,630 (Vaarstra) are related processes.

SUMMARY OF THE INVENTION

[0008] It has been an object of at least one embodiment of the present invention to provide an improved process for CMP.

[0009] Another object of at least one embodiment of the present invention has been that, at the conclusion of said process there be no oxide layer present on the surface of a metal that has been subjected to said process.

[0010] Still another object of at least one embodiment of the present invention has been that, at the conclusion of said process there be no particles of slurry abrasive present on the surface of a metal that has been subjected to said process.

[0011] A further object of at least one embodiment of the present invention has been that said process be suitable for use with tungsten and copper.

[0012] Yet another object of at least one embodiment of the present invention has been to provide a process to easily render hydrophobic a surface that is normally hydrophilic.

[0013] These objects have been achieved by adding to the slurry a quantity of TMAH or TBAH. This has the effect of rendering the surface being polished hydrophobic. In that state a residual layer of oxide will not be left on the surface at the conclusion of CMP. Nor will many slurry abrasive particles remain cling to the freshly polished surface. Those that do are readily removed by a simple rinse or buffing. As an alternative, the CMP process may be performed in three stages—first convention CMP, then polishing in a solution of TMAH or TBAH, and finally a gentle rinse or buffing.

BRIEF DESCRIPTION OF THE DRAWINGS

[0014]FIG. 1 is a cross-section showing a cavity over-filled with metal prior to CMP.

[0015]FIG. 2 shows the structure of FIG. 1 at the conclusion of CMP as practiced in the prior art.

[0016]FIG. 3 shows how the surface seen in FIG. 2 can lead to contact resistance between layers.

[0017]FIG. 4 illustrates a surface after CMP according to the teachings of the present invention.

[0018]FIG. 5 shows how contact resistance between layers is eliminated when the structure of FIG. 5 is used.

[0019]FIG. 6 illustrates how the process of the present invention may be implemented as three separate sequential operations.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0020] The key feature of the present invention is the addition to the slurry of a suitable agent to render the surface that is being polished hydrophobic instead of its normal hydrophilic state. We have discovered two such suitable additives. These are Tetramethyl-ammonium-hydroxide (TMAH) and Tetra-butyl-ammonium-hydroxide (TBAH). If either (or both) of these agents is added to the slurry, the surface of the tungsten plug after CMP is as shown in FIG. 4 where surface 42 is seen to be free of both an oxide layer and any clinging residual particles of slurry abrasive. Accordingly, when the next level of metalization 31 is deposited to connect to plug 12 no contact resistance layer is present (see FIG. 5). Typically, the concentration of TMAH in the slurry suspension has been between about 2% and 20% with 5% being preferred, while for TBAH the concentration in the slurry has been between about 2 and 20% with about 10% being preferred.

[0021] An alternative to adding the TMAH or TBAH directly to the slurry is to perform the CMP operation in three stages. This is illustrated in FIG. 6 which shows three CMP stations and a loading/unloading station 64.

[0022] After the wafer has been loaded into holder 67 it is moved to station 61 (that includes a platen and polishing pad that are not explicitly shown) where conventional CMP takes place until the requisite amount of material has been removed. Slurry is dispensed onto the pad surface from dispenser 65 while attachment 66 serves to periodically recondition the pad surface by means of a combing action. Polishing of layer 12 (see FIG. 1) is achieved using a slurry that comprises a suspension of abrasive particles in deionized water, and hydrogen peroxide.

[0023] Once there is no longer any metal on the dielectric surface outside cavity 13, the wafer holder is moved to station 62 where the freshly created metal surface is polished with an aqueous solution of TMAH (concentration between about 2% and 20%, with about 5% being preferred), or TBAH (concentration between about 2% and 20%, with about 10% being preferred). This has the effect of removing any oxide layer from the metal surface. Additionally, this surface is also rendered hydrophobic so that few slurry particles remain on it and those that do are only very loosely attached.

[0024] Next, the wafer is transferred to station 63 where it is gently buffed using deionized water, so that any remaining abrasive particles get removed. Finally, the wafer moves on to station 64 where it is removed and a fresh wafer is loaded in its place. 

What is claimed is:
 1. A process for performing CMP, comprising: providing a dielectric layer having a first surface; forming a cavity in said dielectric layer; onto said first surface depositing a layer of tungsten, whereby said cavity becomes overfilled with tungsten; polishing said tungsten layer with a slurry that comprises a suspension of abrasive particles in deionized water, hydrogen peroxide, and TMAH until said cavity is just filled with tungsten, having a second surface, and there is no tungsten on said first surface; and rinsing said tungsten layer in deionized water whereby there is no oxide layer on said second surface and all of said abrasive particle have been removed.
 2. The process described in claim 1 wherein the TMAH has a concentration in said slurry of between about 2% and 20%.
 3. The process described in claim 1 wherein said abrasive particles are selected from the group consisting of alumina and silica.
 4. The process described in claim 1 wherein said abrasive particles have a mean diameter of between about 1 and 10,000 microns.
 5. A process for performing CMP, comprising: providing a dielectric layer having a first surface; forming a cavity in said dielectric layer; onto said first surface depositing a layer of tungsten, whereby said cavity becomes overfilled with tungsten; polishing said tungsten layer with a slurry that comprises a suspension of abrasive particles in deionized water, hydrogen peroxide, and TBAH until said cavity is just filled with tungsten, having a second surface, and there is no tungsten on said first surface; and rinsing said tungsten layer in deionized water whereby there is no oxide layer on said second surface and all of said abrasive particle have been removed.
 6. The process described in claim 5 wherein the TBAH has a concentration in said slurry of between about 2% and 20%.
 7. The process described in claim 5 wherein said abrasive particles are selected from the group consisting of alumina and silica.
 8. The process described in claim 5 wherein said abrasive particles have a mean diameter of between about 1 and 10,000 microns.
 9. A process for performing CMP, comprising: providing a dielectric layer having a first surface; forming a cavity in said dielectric layer; onto said first surface depositing a layer of tungsten, whereby said cavity becomes overfilled with tungsten; on a first platen, polishing said tungsten layer with a slurry that comprises a suspension of abrasive particles in deionized water, and hydrogen peroxide until said cavity is just filled with tungsten, having a second surface, and there is no tungsten on said first surface; on a second platen, polishing said second surface with an aqueous solution of TMAH, whereby there is no oxide layer on said second surface; and on a third platen, buffing said second surface with deionized water whereby all of said abrasive particles get removed.
 10. The process described in claim 9 wherein the TMAH has a concentration in said aqueous solution of between about 2% and 20%.
 11. The process described in claim 9 wherein said abrasive particles are selected from the group consisting of alumina and silica.
 12. The process described in claim 9 wherein said abrasive particles have a mean diameter of between about 1 and 10,000 microns.
 13. A process for performing CMP, comprising: providing a dielectric layer having a first surface; forming a cavity in said dielectric layer; onto said first surface depositing a layer of tungsten, whereby said cavity becomes overfilled with tungsten; on a first platen, polishing said tungsten layer with a slurry that comprises a suspension of abrasive particles in deionized water, and hydrogen peroxide until said cavity is just filled with tungsten, having a second surface, and there is no tungsten on said first surface; on a second platen, polishing said second surface with an aqueous solution of TBAH, whereby there is no oxide layer on said second surface; and on a third platen, buffing said second surface with deionized water whereby all of said abrasive particles get removed.
 14. The process described in claim 13 wherein the TBAH has a concentration in said aqueous solution of between about 2% and 20%.
 15. The process described in claim 13 wherein said abrasive particles are selected from the group consisting of alumina and silica.
 16. The process described in claim 13 wherein said abrasive particles have a mean diameter of between about 1 and 10,000 microns.
 17. A surface treatment process, comprising: providing a hydrophillic surface; polishing said surface with a slurry that comprises a suspension of abrasive particles in deionized water and TMAH, whereby said surface is rendered hydrophobic; and thereby causing all of said abrasive particles to be removed when said surface is rinsed in deionized water.
 18. The process described in claim 17 wherein the TMAH has a concentration in said deionized water of between about 2% and 20%.
 19. The process described in claim 17 wherein said abrasive particles are selected from the group consisting of alumina and silica.
 20. The process described in claim 17 wherein said abrasive particles have a mean diameter of between about 1 and 10,000 microns. 21 The process described in claim 17 wherein said hydrophilic surface is selected from the group consisting of tungsten, silicon oxide, and copper.
 22. A surface treatment process comprising: providing a hydrophillic surface; polishing said surface with a slurry that comprises a suspension of abrasive particles in deionized water and TBAH, whereby said surface is rendered hydrophobic; and thereby causing all of said abrasive particles to be removed when said surface is rinsed in deionized water.
 23. The process described in claim 22 wherein the TBAH has a concentration in said deionized water of between about 2 and 20%.
 24. The process described in claim 22 wherein said abrasive particles are selected from the group consisting of alumina and silica.
 25. The process described in claim 22 wherein said abrasive particles have a mean diameter of between about 1 and 10,000 microns.
 26. The process described in claim 22 wherein said hydrophilic surface is selected from the group consisting of tungsten, silicon oxide, and copper.
 27. A process for performing CMP, comprising: providing a dielectric layer having a first surface; forming a cavity in said dielectric layer; onto said first surface depositing a layer of copper, whereby said cavity becomes overfilled with copper; polishing said copper layer with a slurry that comprises a suspension of abrasive particles in deionized water, hydrogen peroxide, and TMAH until said cavity is just filled with copper, having a second surface, and there is no copper on said first surface; and rinsing said copper layer in deionized water whereby there is no oxide layer on said second surface and all of said abrasive particle have been removed.
 28. The process described in claim 27 wherein the TMAH has a concentration in said slurry of between about 2% and 20%.
 29. A process for performing CMP, comprising: providing a dielectric layer having a first surface; forming a cavity in said dielectric layer; onto said first surface depositing a layer of copper, whereby said cavity becomes overfilled with copper; polishing said copper layer with a slurry that comprises a suspension of abrasive particles in deionized water, hydrogen peroxide, and TBAH until said cavity is just filled with copper, having a second surface, and there is no copper on said first surface; and rinsing said copper layer in deionized water whereby there is no oxide layer on said second surface and all of said abrasive particle have been removed.
 30. The process described in claim 29 wherein the TBAH has a concentration in said slurry of between about 2% and 20%. 